Polyamide PA6
PA6 has good comprehensive properties, including mechanical properties, heat resistance, abrasion resistance,
chemical resistance and self-lubrication, low friction coefficient, certain flame retardancy, easy processing, and
is suitable for filling with glass fiber and other fillers to enhance the modification, improve the performance and
expand the scope of application.
Technical index
| Typical Properties |
Test Method |
Test Condition |
Value |
Unit |
| Relative Viscosity |
Q/321291WHY001 |
96%H2SO4 |
2.70±0.04 |
% |
| Moisture |
Q/321291WHY001 |
/ |
≤0.06 |
% |
| Hot Water Extract Content |
Q/321291WHY001 |
/ |
≤0.5 |
% |
| Density |
ISO1183 |
23ºC |
1.119 |
g/cm³ |
| Melt Flow Rate |
ISO1133 |
250ºC/0.325kg |
3.2 |
g/min |
| Tensile Stress |
ISO527 |
50mm/min |
76 |
Mpa |
| Elongation at Break |
|
50mm/min |
42 |
% |
| Tensile Modulus |
|
50mm/min |
3.7 |
Gpa |
| Flexural Strength |
ISO178 |
2mm/min |
98.8 |
Mpa |
| Flexural Modulus |
ISO178 |
2mm/min |
2.6 |
Gpa |
Applications
It is suitable for manufacturing wear-resistant parts, transmission structure parts, household electrical parts,
automobile manufacturing parts, screw rod prevention mechanical parts, chemical machinery parts and
chemical equipment. Such as turbine, gear, bearing, impeller, crank, instrument panel, drive shaft, valve,
blade, screw rod, high-pressure washer, screw, nut, sealing ring, shuttle, sleeve, shaft sleeve connector, etc.
Package
25kg per bag, 40 bag per pallet